In vitro and in vivo evaluation of the biocompatibility of a calcium phosphate/poly(lactic-co-glycolic acid) composite

This study assess the effects of bioceramic and poly(lactic-co-glycolic acid) composite (BCP/PLGA) on the viability of cultured macrophages and human dental pulp fibroblasts, and we sought to elucidate the temporal profile of the reaction of pulp capping with a composite of bioceramic of calcium phosphate and biodegradable polymer in the progression of delayed dentine bridge after (30 and 60 days) in vivo. Histological evaluation of inflammatory infiltrate and dentin bridge formation were performed after 30 and 60 days. There was similar progressive fibroblast growth in all groups and the macrophages showed viability. The in vivo study showed that of the three experimental groups: BCP/PLGA composite, BCP and calcium hydroxide (Ca(OH)(2)) dentin bridging was the most prevalent (90 %) in the BCP/PLGA composite after 30 days, mild to moderate inflammatory response was present throughout the pulp after 30 days. After 60 days was observed dentine bridging in 60 % and necrosis in 40 %, in both groups. The results indicate that understanding BCP/PLGA composite is biocompatible and by the best tissue response as compared to calcium hydroxide in direct pulp capping may be important in the mechanism of delayed dentine bridge after 30 and 60 days.

Biocompatibility of New Calcium Aluminate Cement (Endo Binder)

Introduction: The purpose of this study was to evaluate the biocompatibility of calcium aluminate cement (EndoBinder) in subcutaneous tissue of rats. Methods: Fifteen rats, weighing 300 g, were separated into 3 groups (n = 5) in accordance with the time of death (7, 21, 42 days). Two incisions were made in the dorsal subcutaneous tissue of each rat in which were implanted 2 polyethylene tubes filled with the test materials, Endo Binder (EB) and Grey MTA (GMTA). The external tube walls were considered the negative control group (CG). After 7, 21, and 42 days, animals were killed, obtaining 5 samples per group, at each time interval of analysis. Results: From the morphologic and morphometric analyses by using a score of (0-3) (50, 100, and 400x), results showed absence of inflammatory reaction (0) for EB after 42 days. However, for GMTA, a slight inflammatory reaction (1) was observed after 42 days, which means the persistence of a chronic inflammatory process. When compared with CG, tissue reaction ranging from discrete (1-7 days) to absent (0-42 days) was observed. Conclusions: EndoBinder presented satisfactory tissue reaction; it was biocompatible when tested in subcutaneous tissue of rats. (J Endod 2012;38:367-371)

Biocompatibility and setting time of CPM-MTA and white Portland cement clinker with or without calcium sulfate

To evaluate the biocompatibility and the setting time of Portland cement clinker with or without 2% or 5% calcium sulfate and MTA-CPM. Twenty-four mice (Rattus norvegicus) received subcutaneously polyethylene tubes filled with Portland cement clinker with or without 2% or 5% calcium sulfate and MTA. After 15, 30 and 60 days of implantation, the animals were killed and specimens were prepared for microscopic analysis. For evaluation of the setting time, each material was analyzed using Gilmore needles weighing 113.5 g and 456.5 g, according to the ASTM specification Number C266-08 guideline. Data were analyzed by ANOVA and Tukey's test for setting time and Kruskal-Wallis and Dunn test for biocompatibility at 5% significance level. Histologic observation showed no statistically significant difference of biocompatibility (p>0.05) among the materials in the subcutaneous tissues. For the setting time, clinker without calcium sulfate showed the shortest initial and final setting times (6.18 s/21.48 s), followed by clinker with 2% calcium sulfate (9.22 s/25.33 s), clinker with 5% calcium sulfate (10.06 s/42.46 s) and MTA (15.01 s/42.46 s). All the tested materials showed biocompatibility and the calcium sulfate absence shortened the initial and final setting times of the white Portland cement clinker

Periapical Tissue Response After Use of Intermediate Restorative Material, Gutta-Percha, Reinforced Zinc Oxide Cement, and Mineral Trioxide Aggregate as Retrograde Root-End Filling Materials: A Histologic Study in Dogs

Purpose: To investigate the periapical tissue response of 4 different retrograde root-filling materials, ie, intermediate restorative material, thermoplasticized gutta-percha, reinforced zinc oxide cement (Super-EBA), and mineral trioxide aggregate (MTA), in conjunction with an ultrasonic root-end preparation technique in an animal model. Materials and Methods: Vital roots of the third and fourth right mandibular premolars in 6 healthy mongrel dogs were apicectomized and sealed with 1 of the materials using a standardized surgical procedure. After 120 days, the animals were sacrificed and the specimens were analyzed radiologically, histologically, and scanning electron microscopically. The Fisher exact test was performed on the 2 outcome values. Results: Twenty-three sections were analyzed histologically. Evaluation showed better re-establishment of the periapical tissues and generally lower inflammatory infiltration in the sections from teeth treated with the intermediate restorative material and the MTA. New root cement on the resected dentin surfaces was seen on all sections regardless of the used material. New hard tissue formation, directly on the surface of the material, was seen only in the MTA sections. There was no statistical difference in outcome among the tested materials. Conclusions: The results from this dog model favor the intermediate restorative material and MTA as retrograde fillings when evaluating the bone defect regeneration. MTA has the most favorable periapical tissue response when comparing the biocompatibility of the materials tested. (C) 2012 American Association of Oral and Maxillofacial Surgeons J Oral Maxillofac Surg 70:2041-2047, 2012

Effect of whitening toothpaste on titanium and titanium alloy surfaces

Dental implants have increased the use of titanium and titanium alloys in prosthetic applications. Whitening toothpastes with peroxides are available for patients with high aesthetic requirements, but the effect of whitening toothpastes on titanium surfaces is not yet known, although titanium is prone to fluoride ion attack. Thus, the aim of the present study was to compare Ti-5Ta alloy to cp Ti after toothbrushing with whitening and conventional toothpastes. Ti-5Ta (%wt) alloy was melted in an arc melting furnace and compared with cp Ti. Disks and toothbrush heads were embedded in PVC rings to be mounted onto a toothbrushing test apparatus. A total of 260,000 cycles were carried out at 250 cycles/minute under a load of 5 N on samples immersed in toothpaste slurries. Surface roughness and Vickers microhardness were evaluated before and after toothbrushing. One sample of each material/toothpaste was analyzed by Scanning Electron Microscopy (SEM) and compared with a sample that had not been submitted to toothbrushing. Surface roughness increased significantly after toothbrushing, but no differences were noted after toothbrushing with different toothpastes. Toothbrushing did not significantly affect sample microhardness. The results suggest that toothpastes that contain and those that do not contain peroxides in their composition have different effects on cp Ti and Ti-5Ta surfaces. Although no significant difference was noted in the microhardness and roughness of the surfaces brushed with different toothpastes, both toothpastes increased roughness after toothbrushing.

Epiphany root canal sealer prepared with resinous solvent is irritating to rat subcutaneous tissues

Objective: This study assessed the biocompatibility of the Epiphany endodontic sealer prepared with resinous solvent of Epiphany system (Thinning resin) in rat subcutaneous tissues. Study Design: Polyethylene tubes were filled with the sealer and 4 groups were established: GI, Epiphany prepared with 1 drop of resinous solvent (RS); GII, Epiphany prepared with 1 drop of RS and photoactivated; GIII, Epiphany associated with self-etch primer and prepared with 1 drop of RS; GIV, Epiphany associated with self-etch primer, prepared with 1 drop of RS and photoactivated. The filled tubes were implanted into 4 different regions of the dorsum of 20 adult male rats. Results: After 7, 14 and 21 days, all groups presented a moderate to severe chronic inflammation, necrosis and foreign-body giant cells. At 42 days, although the intensity of chronic inflammatory reaction decreased, the other features still were observed. Conclusion: The Epiphany sealer prepared with the RS was irritating to rat subcutaneous tissues.

Cytocompatibility of Porous Biphasic Calcium Phosphate Granules With Human Mesenchymal Cells by a Multiparametric Assay

This work aims to evaluate the cytocompatibility of injectable and moldable restorative biomaterials based on granules of dense or porous biphasic calcium phosphates (BCPs) with human primary mesenchymal cells, in order to validate them as tools for stem cell-induced bone regeneration. Porous hydroxyapatite (HA) and HA/beta-tricalcium phosphate (beta-TCP) (60: 40) granules were obtained by the addition of wax spheres and pressing at 20 MPa, while dense materials were compacted by pressing at 100 MPa, followed by thermal treatment (1100 degrees C), grinding, and sieving. Extracts were prepared by 24-h incubation of granules on culture media, with subsequent exposition of human primary mesenchymal cells. Three different cell viability parameters were evaluated on the same samples. Scanning electron microscopy analysis of the granules revealed distinct dense and porous surfaces. After cell exposition to extracts, no significant differences on mitochondrial activity (2,3-bis(2-methoxy-4-nitro-5-sulfophenly)-5-[(phenylamino) carbonyl]-2H-tetrazolium hydroxide) or cell density (Crystal Violet Dye Elution) were observed among groups. However, Neutral Red assay revealed that dense materials extracts induced lower levels of total viable cells to porous HA/beta-TCP (P < 0.01). Calcium ion content was also significantly lower on the extracts of dense samples. Porogenic treatments on BCP composites do not affect cytocompatibility, as measured by three different parameters, indicating that these ceramics are well suited for further studies on future bioengineering applications.

Anatomical and functional evaluation of tympanoplasty using a transitory natural latex biomembrane implant from the rubber tree Hevea brasiliensis

PURPOSE: To compare the role of transitory latex and sylastic (R) implants in tympanoplasty on the closure of tympanic perforations. METHODS: A randomized double-blind prospective study was conducted on 107 patients with chronic otitis media submitted to underlay tympanoplasty and divided at random into three groups: control with no transitory implant, latex membrane group, and sylastic (R) membrane group. RESULTS: Greater graft vascularization occurred in the latex membrane group (p<0.05). Good biocompatibility was obtained with the use of the latex and silicone implants, with no effect on the occurrence of infection, otorrhea or otorragy. CONCLUSION: The use of a transitory latex implant induced greater graft vascularization, with a biocompatible interaction with the tissue of the human tympanic membrane.

Study of the osteoconductive capacity of hydroxyapatite implanted into the femur of ovariectomized rats

Osteoporosis is a global public health that affects postmenopausal women due to the deficiency of estrogen, a hormone that plays an important role in the microarchitecture of bone tissue. Osteoporosis predisposes to pathological bone fracture that can be repaired by conventional methods. However, depending on the severity and quantity of bone loss, the use of autogenous grafts or biomaterials such as hydroxyapatite might be necessary. The latter has received increasing attention in the medical field because of its good biological properties such as osteoconductivity and biocompatibility with bone tissue. The objective of this study was to evaluate using histologic and radiographic analyses, the osteogenic capacity of hydroxyapatite implanted into the femur of rats with ovariectomy-induced osteoporosis. Eighteen rats were divided into three groups with six animals in each: group nonovariectomized, bilaterally ovariectomized not receiving estrogen replacement therapy, and bilaterally ovariectomized submitted to estrogen replacement therapy. Defects were created experimentally in the distal epiphysis of the femur with a surgical drill and filled with porous hydroxyapatite granules. The animals were sacrificed 8 weeks after surgery. The volume of newly formed bone in the implant area was quantified by morphometrical methods. The results were analyzed by ANOVA followed by the Tukey test (P < 0.05). The hydroxyapatite granules showed good radiopacity. Histological analysis revealed less quantity of newly formed bone in the ovariectomized group not submitted to hormone replacement therapy. In conclusion, bone neoformation can be expected even in bones compromised by estrogen deficiency, but the quantity and velocity of bone formation are lower. Microsc. Res. Tech., 2011. (c) 2011 Wiley Periodicals, Inc.

Staining of the Internal Limiting Membrane with the Use of Heavy Brilliant Blue G

Background: Brilliant blue G (BBG) is frequently used in chromovitrectomy to facilitate internal limiting membrane (ILM) peeling. A study was initiated to evaluate if heavy BBG is safe and effective in staining the ILM. Methods: We studied 30 eyes, 23 with idiopathic macular holes and 7 of patients with diabetic macular edema. Removal of the ILMs was assisted by heavy BBG staining. In cases with histopathological correlation the ILMs were evaluated with hematoxylin and eosin, Masson's trichrome, periodic acid-Schiff and glial fibrillary acidic protein staining. In addition, immunohistochemistry was also performed using specific antibodies for vimentin, neuron-specific enolase, factor VIII and CD68. Using the Image-Pro Plus software of Media Cybernetics Co. we found an average thickness in ILMs. Results: Of the ILM specimens sent, 19/30(63.33%) could not be processed properly because of the limited sample material, recognizing only fragments of dispersed fibrillar material. In macular hole ILMs we found an average thickness of 1.3 +/- 0.65 mu m, and in diabetic macular edema ILMs an average thickness of 6.2 +/- 1.4 mu m. Conclusions: In heavy BBG-assisted ILM peeling we observed no intraoperative or postoperative complications after a mean follow-up of 12 months. Heavy BBG could be an effective and safe vehicle for staining the ILM. Copyright (C) 2012 S. Karger AG, Basel

Response of mice connective tissue to intracanal dressings containing chlorhexidine

Substances containing chlorhexidine (CHX) have been studied as intracanal medicaments. The aim of the present study was to characterize the response of mouse subcutaneous connective tissue to CHX-containing medications by conventional optical microscopy. The tissue response was evaluated by implanting polyethylene tubes containing one of the substances evaluated: Calen paste + 0.5% CHX, Calen + 2% CHX, 2% CHX gel, and Calen paste (control). After experimental periods of 7, 21, and 63 days, the implants (n = 10) were removed along with the subcutaneous connective tissue. Tissue samples were subjected to histological processing, and sections were stained with hematoxylin and eosin. Qualitative and quantitative analyses of the number of inflammatory cells, blood vessels, and vascularized areas were performed. Results were analyzed by ANOVA and Tukey tests with the significance level set at 5%. We concluded that Calen + 0.5% CHX led to reparative tissue response in contrast with Calen + 2% CHX and 2% CHX gel, which induced persistent inflammatory response, pointing to the aggressive nature of this mixture. When Calen + 2% CHX and 2% CHX gel were compared, the latter induced more intense inflammatory response. Microsc. Res. Tech., 2012. (C) 2012 Wiley Periodicals, Inc.

Rat subcutaneous tissue response to MTA Fillapex® and Portland cement

The aim of this study was to evaluate the response of rat subcutaneous tissue to MTA Fillapex® (Angelus), an experimental root canal filling material based on Portland cement and propylene glycol (PCPG), and a zinc oxide, eugenol and iodoform (ZOEI) paste. These materials were placed in polyethylene tubes and implanted into the dorsal connective tissue of Wistar rats for 7 and 15 days. The specimens were stained with hematoxylin and eosin, and evaluated regarding inflammatory reaction parameters by optical microscopy. The intensity of inflammatory response against the sealers was analyzed by two blinded and previously calibrated examiners for all experimental periods (kappa=0.96). The histological evaluation showed that all materials caused a moderate inflammatory reaction at 7 days, which subsided with time. A greater inflammatory reaction was observed at 7 days in the tubes filled with ZOEI paste. Tubes filled with MTA Fillapex presented some giant cells, macrophages and lymphocytes after 7 days. At 15 days, the presence of fibroblasts and collagen fibers was observed indicating normal tissue healing. The tubes filled with PCPG showed similar results to those observed in MTA Fillapex. At 15 days, the inflammatory reaction was almost absent at the tissue, with several collagen fibers indicating normal tissue healing. Data were analyzed by the nonparametric Kruskal-Wallis test (?=0.05). Statistically significant difference (p<0.05) was found only between PCPG at 15 days and ZOEI at 7 days groups. No significant differences were observed among the other groups/periods (p>0.05). MTA Fillapex and Portland cement added with propylene glycol had greater tissue compatibility than the PCPG paste.

In vivo evaluation of tissue response to new endodontic sealers

Introduction: The sealers can be in direct contact with the periapical tissues. Thus, these materials must have appropriate physical and biological properties, providing conditions for repair to occur. Objective: The aim of this study was to evaluate the response of rat subcutaneous tissue to endodontics sealers. Material and methods: Three materials comprised the groups: group I – Zinc Oxide, Eugenol and Iodoform paste, group II – Portland cement with propylene glycol, and group III – MTA Fillapex® (Angelus). These materials were placed in polyethylene tubes and implanted into dorsal connective tissue of Wistar rats for seven and 15 days. The specimens were stained with hematoxylin and eosin and evaluated regarding to inflammatory reaction parameters through a light microscope. The data were compared using Kruskal-Wallis test with significance level of 5%. The intensity of inflammatory response against the sealers was analyzed by two blinded and previously calibrated observers for all experimental periods. Results: The histological evaluation showed that all the materials caused a moderated inflammatory reaction at seven days which decreased with time. A greater inflammatory reaction was observed at seven days in group I. The other specimens had significantly less inflammatory cells when compared to this group. Tubes with MTA Fillapex® presented some giant cells, macrophages and lymphocytes after seven days. At 15 days, the presence of fibroblasts and collagen fibers was observed indicating normal tissue healing. The group II showed similar results to those observed in MTA Fillapex® already at seven days. At 15 days the inflammatory reaction presented was almost absent at the tissue, with many collagen fibers indicating normal tissue healing. Statistical analysis showed a significant statistical difference amongst the group I (seven days) and II (15 days) (p < 0.05). In the other groups no (Continue)

In vivo evaluation of tissue response to new endodontic sealers

Introduction: The sealers can be in direct contact with the periapical tissues. Thus, these materials must have appropriate physical and biological properties, providing conditions for repair to occur. Objective: The aim of this study was to evaluate the response of rat subcutaneous tissue to endodontics sealers. Material and methods: Three materials comprised the groups: group I – Zinc Oxide, Eugenol and Iodoform paste, group II – Portland cement with propylene glycol, and group III – MTA Fillapex® (Angelus). These materials were placed in polyethylene tubes and implanted into dorsal connective tissue of Wistar rats for seven and 15 days. The specimens were stained with hematoxylin and eosin and evaluated regarding to inflammatory reaction parameters through a light microscope. The data were compared using Kruskal-Wallis test with significance level of 5%. The intensity of inflammatory response against the sealers was analyzed by two blinded and previously calibrated observers for all experimental periods. Results: The histological evaluation showed that all the materials caused a moderated inflammatory reaction at seven days which decreased with time. A greater inflammatory reaction was observed at seven days in group I. The other specimens had significantly less inflammatory cells when compared to this group. Tubes with MTA Fillapex® presented some giant cells, macrophages and lymphocytes after seven days. At 15 days, the presence of fibroblasts and collagen fibers was observed indicating normal tissue healing. The group II showed similar results to those observed in MTA Fillapex® already at seven days. At 15 days the inflammatory reaction presented was almost absent at the tissue, with many collagen fibers indicating normal tissue healing. Statistical analysis showed a significant statistical difference amongst the group I (seven days) and II (15 days) (p < 0.05). In the other groups no significant statistical differences were observed. Conclusion: MTA Fillapex® and Portland cement with propylene glycol were more biocompatible than the other tested cements.

Cytotoxicity tests for nanostructured chitosan/PEO membranes using the agar diffusion method

Electrospinning is used to produce fibers in the nanometer range by stretching a polymeric jet using electric fields of high magnitude. Chitosan is an abundant natural polymer that can be used to obtain biocompatible nanostructured membranes. The objectives of this work were to obtain nanostructured membranes based on blends of chitosan and polyoxyethylene (PEO), and evaluate their thermal and morphological properties, as well as their in vitro biocompatibility by agar diffusion cytotoxicity tests for three different cell lines. A nanostructured fibrous membrane with fiber diameters in the order of 200 nm was obtained, which presented a rough surface and thickness ranging from one to two millimeters. The results of the cytotoxicity tests evidenced that the chitosan/PEO membranes are non-toxic to the cells studied in this work. Further, the electrospinning technique was effective in obtaining nanostructured chitosan/PEO membranes, which showed biocompatibility according to in vitro preliminary tests using the cell lines.